Epoxy-Coat is a modified cycloaliphatic formulated for high build applications on concrete or
wood floors. It will create a hard, tough film with abrasion resistance, chemical resistance with less yellowing than standard aliphatic epoxies. Complies with all VOC and VOS regulations
TYPICAL PROPERTIES
Solids-100%
Color-Clear
Flash Point, Setaflash, F-230
Pounds/gallon- 8.44
Mixed Viscosity, cps with Part B activator -600-2000
Application recommended thickness from 16 mils DFT to 1/2
Solvent odor - None
DRYING CHARACTERISTICS
Based on 70 degrees F surface and environment temperatures:
Surface dry for traffic-18 hours
Surface dry for re-coat -0-12
Note: Color coats may be longer
Full Cure- 7 days
MIXING INSTRUCTION
Add top contents with bottom contents.
Mix thoroughly with a jiffy type mixer for 3 minutes and then box mix before using.
Refer to PERFORMANCE paint product mixing instruction for more details.
APPLICATION METHOD
Squeegee and back roll with thin nap roller.
Recommended surface preparation is mechanical shotblasting or scarifying.
Prolonged or frequent contact with the resin (Part A) may cause dermatitis, sensitization, or other allergic responses. Good industrial hygiene practices should be observed in working with these materials. Before using them, consult the applicable Material Safety Data Sheets for appropriate handling procedures and protective equipment.
STORAGE
E-350 should be stored in tightly sealed containers at normal room temperatures. Color of the curing agent may darken during long-term storage, the extent of color formation depending on storage temperature and degree of exposure to air.
PRECAUTIONS
The curing agent (Part B) may cause chemical burns in eyes or on skin, sensitization or other allergic responses, and can cause respiratory irritation. In large quantities, uncontrolled mixing with epoxy resins can result in runaway exothermic reactions.
Caution: Non-skid additives should be used where slipperiness may be a problem.
CURED STATE PROPERTIES
Heat Deflection Temperature C-48
Tensile Strength, psi -5349
Tensile Elongation at break, percent - 16
Compressive Strength, Ultimate, psi-19,800
Compressive Yield Strength, psi -0.98
Izod Impact, ft-lb/inch notch -.606
Taber Abrasion CS-17, 1000 G., 1000 cycles-38 mg. wt. loss
Reported as percent weight change of immersed 1” by 3” by 1/8” samples at 25 degrees C. ONE WEEK
5% Detergent - .58
5% Acetic Acid - .71
20% Acetic Acid- 3.31
50% Acetic Acid- Destroyed
10% Sulfuric Acid - .77
25% Sulfuric Acid - .69
70% Sulfuric Acid - .11
98% Sulfuric Acid -Destroyed
5% Nitric Acid- .74
20% Nitric Acid-1.35
10% Hydrochloric Acid-.51
10% Sodium Hydroxide- .45
50% Sodium Hydroxide-.03
5% Citric Acid-.60
5% Lactic Acid -.59
Methyl Ethyl Ketone-Destroyed
Xylene -.09
Toluene- .18
Ethanol -7.06
Methanol- Destroyed
Isopropanol-.26
Gasoline-.05
Antifreeze-.02
Brake Fluid - .89
Transmission Fluid-.09
Skydrol (500B4)- .01
Bleach-.45
3% Hydrogen Peroxide -.59
50% Sugar Solution -.49